PU sheets/PU insulation sheet/pu plate

FOB Reference Price:Get Latest Price
US $100-200 / Square Meter | 10 Square Meter/Square Meters (Min. Order)
Supply Ability:
2000 Square Meter/Square Meters per Month
Port:
Shanghai Port,Tianjin Port or Qingdao Port
Report Suspicious Activity
Overview
Quick Details
Place of Origin:
Henan, China (Mainland)
Brand Name:
Qianjin
Model Number:
QJ703
Material:
PU etc.
Color:
Red,Yellow,Green,etc.
Hardness:
20A-75D
Elastic Resilience:
20%-45%
Abrasion(g/1.6km):
0.02-0.045
Anti-Abrasion(KN/m):
50KN/m-195KN/m
Elongation(Mpa):
30Mpa-55Mpa
Tensile Strengh:
220%-760%
Type of enterprise:
Manufacturing enterprise
Product Packaging:
Wooden case or as your requirement
Packaging & Delivery
Packaging Details
Wooden case or others
Delivery Time
Twenty or thirty days

Specifications

1) Excellent price performance ratio
2) Various color, smooth surface
3) 100% PU raw material
4)ISO9001

1.:Proportioning

   HL1336 : MOCA =100 : 10.65

2.:Craft

   (1).As the material is solid under the normal temperature,so it should be placed in 

        a 90 celsiuss oven to be heated before using to make it melt.

   (2).Taking a proper amount of the material in a container,make a degassing when 

         it is heated  to 90 celsius,until it without larger bubbles when visual.

   (3).Heat the MOCA until melting,mix up the two when the temperature of the 

        material is about 80 celsius,and then stir fast. 

   (4).Pouring the material to a 100 celsiuss mould,die after gel,open the mould 

        after about an hour.

   (5).Put the products to a 100 celsiuss oven ,make a vulcanization,it can have a 

        stable performance after 12-16 hours.

3.:Announcements:

   (1).The material should be timely sealed when it be taken out to prevent a moisture 

         absorrtion.

   (2).The material should be keep in a cool and ventilate place.

                                   Operation Technology and physical index 

 

Prepolymer NCO content

3.60

Proportioning:Prepolymer/MOCA(mass ratio)

100/10.65

 

Suggest mixing temperature

Prepolymer(°C)

 

80

 

MOCA(°C)

 

110-120

  

Moulding vulcanization temperature(°C)

 

105-110

  

Additional vulcanization (°C*hour)

 

(100-110)*(12-16)

        

physical index

 

Hardness 

(shore A)

  85
 

Tensile strength 

(Mpa)

 

44.01

 

 

Tearing strength (KN/m)

 

 

107.14

 

Elongation (%)

 

727.92

 

Permanent deformation (%)

 

5.17

 

Abrasion (cm3/1.61km)

 

0.0192

 

Spring back (%)

 

33

 

 

                              The data sheet of the PU sieve plate